Super Duplex 2507 Bright Bars

₹480

Quality Stainless Steel Bright Bars Super Duplex 2507 at Lowest Prices!

Are you looking for a genuine and professional manufacturer and supplier of 2507 super duplex stainless steel bright bars? Call us now at +919930002070! or Email Us on sales@asiametsteel.com

We have an extensive collection of stainless steel super duplex 507 bright bars for sale with diameters ranging from 3mm to 300mm. A standard length is 5-6 MTRS, but we can cut to any length. Stainless steel super duplex 2507 bright bars are mainly used for structural and machining application in a wide range of industries. Our stainless steel bright super duplex 2507 bar drawing process ensures an enhanced surface, higher strength and closer tolerances.

Why Choose Asiamet as your Supplier for Super Duplex 2507 Steel Bright Bars, UNS S32750/S32950, 1.4410 SS bright Bars?

Competitive or Lowest Prices for 2507 Stainless Steel Super Duplex Bright Bars – At Asiamet, we are committed to provide our customers with lowest possible prices for stainless steel super duplex 2507 bars. With higher volumes, we can also offer quantity discounts.
Certification & Testing for 2507 Stainless Steel Super Duplex Bright Bars – All our products are supplied with Test Certificates, as per EN 10204 3.1 and/or NABL approved Lab Testing Reports
Short Lead Times for 2507 Stainless Steel Super Duplex Bright Bars– Since we are a leading stockholder and direct mill buyer of stainless steel 304 bars, we can offer delivery of cut to length stainless steel bars in 1 or 2 days. For production quantities, we can supply stainless steel super duplex bars with shortest possible lead times.
In House 2507 Stainless Steel Super Duplex Bright Bars Processing Facilities – We have in house stainless steel super duplex 2507 bars processing facilities enabling us to deliver the product in various forms other than standard sizes.

Categories: Stainless Steel, Steel Bars & Rods

Description
Reviews (0)

Description

Stainless Steel Super Duplex 2507 Bright Bars, UNS S32750/S32950, 1.4410 Manufacturers & Suppliers in India – Cold Drawn Bright Bars, Peeled Bars Manufacturers

Asiamet is one of the biggest manufacturers and suppliers of stainless steel bright bars in 200, 300 and 400 series. We can supply stainless steel bright bars in size range of 8mm dia to 250mm dia, at the most competitive prices in the industry. Stainless steel bright bars supplied by Asiamet, are widely used in many industries. Finishes on stainless steel bright bars can vary and include cold drawn, centerless ground, smooth turned, rough turned, turned ground and polished.

Production & Stock Range for Stainless Steel Super Duplex 2507 Bright Bars, UNS S32750 / S32950, 1.4410 SS Bright Bars

Product	Stainless Steel Super Duplex 2507
Specifications	ASTM/ASME A/SA276, ASTM/ASME A/SA479, ASTM/ASME A/SA 484
Length	Upto 6 Meters
Size	3mm up to 520mm
Ultrasonic Test	100% tested through Digital Ultrasonic Flaw Detector, as per ASTM A-388, EN 10308 (Class 1 to 4), API 6A/ISO 10423:2003-PSL 3, SEP 1920:1984 (class A, B, C), MIL STD 2154
Surface Finish	Black, Peeled, Polished, Bright, Hair Line, Brush, Sand Blast
Type	Hot Rolled, Cold Drawn, Centerless Grinding, Forged
Size Tolerances	H9, H10, H11, K12, K13, A-484, EN-10060, DIN-1013
Value Added Services	Laser Cutting, Polishing, Grinding, Heat Treating, Saw Cutting, Forming, Rolling, Shearing
Manufacturers	Viraj, Mukund, Laxcon, Imported, Jindal, Other Indian Manufacturers
Origin of Goods	India, Europe, Japanese, UK, Korea, Thailand, Taiwan.
Export Countries	Saudi Arabia, Tanzania, Africa, Nigeria, Qatar, Oman, UAE and Other Middle East Nations
Delivery Time	Immediate for Goods in Ready Stock, 10-40 Days for Production QTY’s
Packing	Wooden Pallets, Export Sea-Worthy Packing
Applications	Off-Shore Oil Drilling Companies, Power Generation, Petrochemicals, Gas Processing, Specialty Chemicals, Pharmaceuticals, Pharmaceutical Equipment, Chemical Equipment, Sea Water Equipment, Heat Exchangers, Condensers, Pulp and Paper Industry
Test Certificates	As per EN 10204 3.1
Inspection	Seller Inspection, Buyer Inspection or Third Party Inspection

Chemical Composition (%) of Super Duplex 2507 Steel Bright Bars, UNS S32750 / S32950, 1.4410 SS Bright Bars

Grade	C≤	Si≤	Mn≤	P≤	S≤	Ni	Cr
super duplex 2507	0.30	0.80	1.20	0.35	0.80	6 – 8	24 – 26

Mechanical Properties of Super Duplex 2507 Steel Bright Bars, UNS S32750 / S32950, 1.4410 SS Bright Bars

Grades	Density	Melting Point	Tensile Strength	Yield Strength (0.2%Offset)	Elongation
super duplex 2507	7.8 g/cm3	1350 °C (2460 °F)	Psi – 116000 , MPa – 800	Psi – 80000 , MPa – 550	15%

Physical Properties of Super Duplex 2507 Steel Bright Bars, UNS S32750/S32950, 1.4410 SS Bright Bars

Properties	Metric	Imperial
Density	7.8 g/cm3	0.281 lb/in3
Melting point	1350°C	2460°F

Equivalents of Various Grades of Super Duplex 2507 Steel Bright Bars, UNS S32750/S32950, 1.4410 SS Bright Bars

STANDARD	WERKSTOFF NR.	UNS	JIS	BS	GOST	AFNOR	EN
super duplex 2507	1.4410	S32750 / S32950	–	–	–	–	–

Chemical Composition of Various Grades of Stainless Steel Bars

Grade	C≤	Si≤	Mn≤	P≤	S≤	Ni	Cr
201	0.15	1	5.5-7.5	0.5	0.03	3.50-5.50	16.00-18.00
202	0.15	1	7.5-10.0	0.5	0.03	4.00-6.00	17.00-19.00
304	0.08	1	2 .00	0.045	0.03	8.00-11.00	18.00-20.00
304L	0.03	1	2 .00	0.045	0.03	8.00-12.00	18.00-20.00
309	0.2	1	2 .00	0.04	0.03	12.00-15.00	22.00-24.00
309S	0.08	1	2 .00	0.045	0.03	12.00-15.00	22.00-24.00
310	0.25	1.5	2 .00	0.04	0.03	19.00-22.00	24.00-26.00
310S	0.08	1	2 .00	0.045	0.03	19.00-22.00	24.00-26.00
316	0.08	1	2 .00	0.045	0.03	10.00-14.00	16.00-18.00
316L	0.03	1	2 .00	0.045	0.03	10.00-14.00	16.00-18.00
316Ti	0.08	1	2 .00	0.045	0.03	10.00-14.00	16.00-18.00
410	0.15	1	1 .00	0.04	0.03	0.6	11.50-13.50
430	0.12	0.12	1	0.04	0.03	0.6	16.00-18.00

Mechanical Properties of Stainless Steel Bars

Grades	Density	Melting Point	Tensile Strength (min.)	Yield Strength (0.2%Offset) (min.)	Elongation (min.)
304	8.0 g/cm3	1400 °C (2550 °F)	Psi – 75000 , MPa – 515	Psi – 30000 , MPa – 205	35%
304H	8.0 g/cm3	1400 °C (2550 °F)	Psi – 75000 , MPa – 515	Psi – 30000 , MPa – 205	35%
304L	8.0 g/cm3	1400 °C (2550 °F)	Psi – 75000 , MPa – 515	Psi – 30000 , MPa – 205	35%
310	7.9 g/cm3	1402 °C (2555 °F)	Psi – 75000 , MPa – 515	Psi – 30000 , MPa – 205	40%
316	8.0 g/cm3	1400 °C (2550 °F)	Psi – 75000 , MPa – 515	Psi – 30000 , MPa – 205	35%
316L	8.0 g/cm3	1399 °C (2550 °F)	Psi – 75000 , MPa – 515	Psi – 30000 , MPa – 205	35%
316TI	8.0 g/cm3	1399 °C (2550 °F)	Psi – 75000 , MPa – 515	Psi – 30000 , MPa – 205	35%
317	7.9 g/cm3	1400 °C (2550 °F)	Psi – 75000 , MPa – 515	Psi – 30000 , MPa – 205	35%
317L	7.9 g/cm3	1400 °C (2550 °F)	Psi – 75000 , MPa – 515	Psi – 30000 , MPa – 205	35%
321	8.0 g/cm3	1457 °C (2650 °F)	Psi – 75000 , MPa – 515	Psi – 30000 , MPa – 205	35%
347	8.0 g/cm3	1454 °C (2650 °F)	Psi – 75000 , MPa – 515	Psi – 30000 , MPa – 205	35%
904L	7.95 g/cm3	1350 °C (2460 °F)	Psi – 71000 , MPa – 490	Psi – 32000 , MPa – 220	35%
446	7.5 g/cm3	1510 °C (2750 °F)	Psi – 75,000 , MPa – 485	Psi – 40,000 , MPa – 275	20%

Weight Calculation of Stainless Steel Bars

Weight of Stainless Steel Round Bar

Dia ( mm ) X Dia (mm ) X 0.00623 = Wt. Per. Mtr.

Dia ( mm ) X Dia (mm ) X 0.0019 = Wt. Per. Feet.

Weight of Stainless Steel Square Bar

Dia ( mm ) X Dia ( mm ) X 0.00788 = Wt. Per. Mtr

Dia ( mm ) X Dia ( mm ) X 0.0024 = Wt.Per. Feet.

Weight of Stainless Steel Hexagonal Bar

Dia ( mm ) X Dia ( mm ) X 0.00680 = Wt. Per.Mtr

Width ( mm ) X Dia ( mm ) X 0.002072 = Wt. Per Feet

Weight of Stainless Steel Flat Bar

Width (mm ) X Thick ( mm ) X 0.00798 = Wt.Per Mtr.

Width (mm ) X Thick ( mm ) X 0.00243 = Wt.Per Feet.

PREN for various Grades of Stainless Steel

What is PREN?

Pitting resistance equivalent numbers (PREN) are a theoretical way of comparing the pitting corrosion resistance of various types of stainless steels, based on their chemical compositions. In general, the higher PREN-value, the more resistant is the stainless steel to localized pitting corrosion by chloride. The elements which have a significant impact are chromium, molybdenum and nitrogen.

The formula used to calculate PREN is as below:

PREN = %Cr + 3.3(%Mo) + 16(%N)

PREN = 1 × %Cr + 3.3 (%Mo + 0.5 × %W) + 16 × %N

Grade	Type	Cr	Mo	N	PREN
Ferritic
1.4003	–	10.5-12.5	NS	0.030 max	10.5-12.5
1.4016	430	16.0-18.0	NS	NS	16.0-18.0
1.4113	434	16.0-18.0	0.9-1.4	NS	19.0-22.6
1.4509	441	17.5-18.5	NS	NS	17.5-18.5
1.4521	444	17.0-20.0	1.8-2.5	0.030max	23.0-28.7
Austenitic
1.4301	304	17.5-19.5	NS	0.11max	17.5-20.8
1.4311	304LN	17.5-19.5	NS	0.12-0.22	19.4-23.0
1.4401/4	316/316L	16.5-18.5	2.0-2.5	0.11max	23.1-28.5
1.4435	316L (2.5% min Mo)	17.0-19.0	2.5-3.0	0.11max	25.3-30.7
1.4406	316LN	16.5-18.5	2.0-2.5	0.12-0.22	25.0-30.3
1.4539	904L	19.0-21.0	4.0-5.0	0.15max	32.2-39.9
1.4563	Sanicro 28	24.0-26.0	3.0-4.0	0.11max	35.9-43.0
1.4547	254SMO	19.5-20.5	6.0-7.0	0.18-0.25	42.2-47.6
1.4529	1925hMo	19.0-21.0	6.0-7.0	0.15-0.25	41.2-48.1
1.4565	4565S	24.0-26.0	4.0-5.0	0.30-0.60	42.0-52.1
Duplex
1.40621	2202	22	0.4	0.2	26.5
1.4162	2101LDX	21.0-22.0	0.1-0.8	0.20-0.25	24.5-28.6
1.4362	SAF 2304	22.0-24.0	0.1-0.6	0.05-0.20	23.1-29.2
1.4462	SAF 2205	21.0-23.0	2.5-3.5	0.10-0.22	30.8-38.1
1.44102	SAF 2507	24.0-26.0	3.0-4.0	0.24-0.35	> 402
1.45012	Zeron 1002	24.0-26.0	3.0-4.0	0.20-0.30	> 402
1.45072	Ferrinox 2552	24.0-26.0	3.0-4.0	0.20-0.30	> 402

Alternative Grades to Stainless Steel Super Duplex 2507 Grade

Features
303	Stainless steel 303 grade can be used when higher machinability is needed, and lower corrosion resistance, formability and weldability are acceptable.
316	Stainless steel 316 grade can be used when higher resistance to pitting and crevice corrosion is required, in chloride environments.
321	Stainless steel 321 grade can be used when better resistance to temperatures of around 600-900°C is needed. 321 has higher hot strength.
3CR12	Stainless steel 3CR12 can be used when lower cost is required, and the reduced corrosion resistance and resulting discoloration are acceptable.
430	Stainless steel 430 grade is acceptable when a lower cost is required, and the reduced corrosion resistance and fabrication characteristic are acceptable.

Service Temperature of Various Grades of Stainless Steel

Grade	Intermittent service temperature	Continuous service temperature
304	1600°F	1700°F
	(870°C)	(925°C)
316	1600°F	1700°F
	(870°C)	(925°C)
309	1800°F	2000°F
	(980°C)	(1095°C)
310	1900°F	2100°F
	(1035°C)	(1150°C)
410	1500°F	1300°F
	(815°C)	(705°C)
420	1350°F	1150°F
	(735°C)	(620°C)
430	1600°F	1500°F
	(870°C)	(815°C)

Testing of Stainless Steel Bright Bars

Manufacturer’s Test Certificate is Provided – Our materials undergo strict quality tests before dispatching them to our clients. All are materials are supplied with Mill Test Certificates, as per EN 10204 3.1
Various Testing: Mechanical Testing, Hardness Test, Chemical Analysis, Positive Material Identification (PMI), Flattening Test, Micro and Macro Test, Pitting Resistance Test, Flaring Test, Intergranular Corrosion (IGC) Test.

Marking of Stainless Steel Bright Bars

As a standard, Asiamet provides all stainless steel bright bar marked with Manufacturers Name, Size and Heat No., which can be co related with the test certificate for the product.

Packaging of Stainless Steel Bright Bars

Asiamet is one of the best company in for delivery of goods with shortest lead times. Our products like stainless steel bright bar are packed to ensure that there is no damage in transit.