Stainless Steel 304L Bright Bars Manufacturers. Buy 100% UT, 304L Stainless Steel Bright Bars!

///304L Stainless Steel Bright Bars

304L Stainless Steel Bright Bars

185

Quality Stainless Steel Bright Bars 304L at Lowest Prices!

Are you looking for a genuine and professional manufacturer and supplier of stainless steel bars in India? Call us now at +919930002070! or Email Us on sales@asiametsteel.com

We have an extensive collection of stainless steel 304L bright bars for sale with diameters ranging from 3mm to 300mm. A standard length is 5-6 MTRS, but we can cut to any length. Stainless steel 304L bright bars are mainly used for structural and machining application in a wide range of industries. Our stainless steel bright 304L bar drawing process ensures an enhanced surface, higher strength and closer tolerances.

Why Choose Asiamet as your Supplier for Stainless Steel 304L Bars, UNS S30403, 1.4306/1.4307 SS Bars?

  • Competitive or Lowest Prices for Stainless Steel Bright Bars – At Asiamet, we are committed to provide our customers with lowest possible prices for stainless steel bright bars. With higher volumes, we can also offer quantity discounts.
  • Certification & Testing for Stainless Steel Bright Bars – All our products are supplied with Test Certificates, as per EN 10204 3.1 and/or NABL approved Lab Testing Reports
  • Short Lead Times for Stainless Steel Bright Bars– Since we are a leading stockholder and direct mill buyer of stainless steel bright bars, we can offer delivery of cut to width stainless steel bright bars in 1 or 2 days. For production quantities, we can supply stainless steel bright bars with shortest possible lead times.
  • In House Stainless Steel Bright Bars Processing Facilities – We have in house stainless steel bright bars processing facilities enabling us to deliver the product in various forms other than standard sizes.

Description

Stainless Steel 304L Bright Bars, UNS S30400, 1.4301 Manufacturers in India – Cold Drawn Bright Bars, Peeled Bars Manufacturers

Asiamet is one of the biggest manufacturers and suppliers of stainless steel bright bars in 200, 300 and 400 series. We can supply stainless steel bright bars in size range of 8mm dia to 250mm dia, at the most competitive prices in the industry. Stainless steel bright bars supplied by Asiamet, are widely used in many industries. Finishes on stainless steel bright bars can vary and include cold drawn, centerless ground, smooth turned, rough turned, turned ground and polished.

Production & Stock Range for Stainless Steel 304L Bright Bars, UNS S30403, 1.4306 / 1.4307 SS Bright Bars

Product Stainless Steel 304/304L Bars
Standard ASTM/ASME A/SA276, ASTM/ASME A/SA479, ASTM/ASME A/SA 484
Length Upto 6 Meters
Size 3mm up to 520mm
Ultrasonic Test 100% tested through Digital Ultrasonic Flaw Detector, as per ASTM A-388, EN 10308 (Class 1 to 4), API 6A/ISO 10423:2003-PSL 3, SEP 1920:1984 (class A, B, C), MIL STD 2154
Surface Finish Centreless Ground & Belt Polished up to Ra value 0.2 microns (12 RMS) and 24 – 320 Grit Polished
Type Hot Rolled, Cold Drawn, Centerless Grinding, Forged
Size Tolerances H9, H10, H11, K12, K13, A-484, EN-10060, DIN-1013
Value Added Services Laser Cutting, Polishing, Grinding, Heat Treating, Saw Cutting, Forming, Rolling, Shearing
Manufacturers Viraj, Mukund, Laxcon, Imported, Jindal, Other Indian Manufacturers
Origin of Goods India, Europe, Japanese, UK, Korea, Thailand, Taiwan.
Export Countries Saudi Arabia, Tanzania, Africa, Nigeria, Qatar, Oman, UAE and Other Middle East Nations
Delivery Time Immediate for Goods in Ready Stock, 10-40 Days for Production QTY’s
Packing Wooden Pallets, Export Sea-Worthy Packing
Applications Off-Shore Oil Drilling Companies, Power Generation, Petrochemicals, Gas Processing, Specialty Chemicals, Pharmaceuticals, Pharmaceutical Equipment, Chemical Equipment, Sea Water Equipment, Heat Exchangers, Condensers, Pulp and Paper Industry
Test Certificates As per EN 10204 3.1
Inspection Seller Inspection, Buyer Inspection or Third Party Inspection

Chemical Composition (%) of Stainless Steel 304L Bright Bars, UNS S30403, 1.4306/1.4307 SS Bright Bars

Grade C≤ Si≤ Mn≤ P≤ S≤ Ni Cr
304 0.08 1 2 .00 0.045 0.03 8.00-11.00 18.00-20.00
304L 0.03 1 2 .00 0.045 0.03 8.00-12.00 18.00-20.00
304H 0.10 0.75 2.00 0.045 0.03 8.00-10.5 18.00-20.00

Mechanical Properties of Stainless Steel 304L Bright Bars, UNS S30403, 1.4306/1.4307 SS Bright Bars

GRADE Tensile Strength : Unit – ksi (MPa) , Minimum Yeild Strength : 0.2 % Offset , Unit – ksi (MPa) , Minimum Elongation : in 2″, Unit : % , Minimum HARDNESS
304 75 (515) 30 (205) 40 92 HRB max
304L 70 (485) 25 (170) 40 92 HRB max
304H 75 (515) 30 (205) 40 92 HRB max

Equivalents of Various Grades of Stainless Steel 304L Bars, UNS S30403, 1.4306/1.4307 SS Bars

STANDARD WERKSTOFF NR. UNS JIS BS GOST AFNOR EN
SS 304 1.4301 S30400 SUS 304 304S31 08Х18Н10 Z7CN18‐09 X5CrNi18-10
SS 304L 1.4306 / 1.4307 S30403 SUS 304L 3304S11 03Х18Н11 Z3CN18‐10 X2CrNi18-9 / X2CrNi19-11
SS 304H 1.4301 S30409


Chemical Composition of Various Grades of Stainless Steel Bright Bars

Grade C≤ Si≤ Mn≤ P≤ S≤ Ni Cr
201 0.15 1 5.5-7.5 0.5 0.03 3.50-5.50 16.00-18.00
202 0.15 1 7.5-10.0 0.5 0.03 4.00-6.00 17.00-19.00
304 0.08 1 2 .00 0.045 0.03 8.00-11.00 18.00-20.00
304L 0.03 1 2 .00 0.045 0.03 8.00-12.00 18.00-20.00
309 0.2 1 2 .00 0.04 0.03 12.00-15.00 22.00-24.00
309S 0.08 1 2 .00 0.045 0.03 12.00-15.00 22.00-24.00
310 0.25 1.5 2 .00 0.04 0.03 19.00-22.00 24.00-26.00
310S 0.08 1 2 .00 0.045 0.03 19.00-22.00 24.00-26.00
316 0.08 1 2 .00 0.045 0.03 10.00-14.00 16.00-18.00
316L 0.03 1 2 .00 0.045 0.03 10.00-14.00 16.00-18.00
316Ti 0.08 1 2 .00 0.045 0.03 10.00-14.00 16.00-18.00
410 0.15 1 1 .00 0.04 0.03 0.6 11.50-13.50
430 0.12 0.12 1 0.04 0.03 0.6 16.00-18.00

Mechanical Properties of Stainless Steel Bright Bars

Grades Density Melting Point Tensile Strength (min.) Yield Strength (0.2%Offset) (min.) Elongation (min.)
304 8.0 g/cm3 1400 °C (2550 °F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 35%
304H 8.0 g/cm3 1400 °C (2550 °F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 35%
304L 8.0 g/cm3 1400 °C (2550 °F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 35%
310 7.9 g/cm3 1402 °C (2555 °F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 40%
316 8.0 g/cm3 1400 °C (2550 °F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 35%
316L 8.0 g/cm3 1399 °C (2550 °F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 35%
316TI 8.0 g/cm3 1399 °C (2550 °F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 35%
317 7.9 g/cm3 1400 °C (2550 °F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 35%
317L 7.9 g/cm3 1400 °C (2550 °F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 35%
321 8.0 g/cm3 1457 °C (2650 °F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 35%
347 8.0 g/cm3 1454 °C (2650 °F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 35%
904L 7.95 g/cm3 1350 °C (2460 °F) Psi – 71000 , MPa – 490 Psi – 32000 , MPa – 220 35%
446 7.5 g/cm3 1510 °C (2750 °F) Psi – 75,000 , MPa – 485 Psi – 40,000 , MPa – 275 20%

Weight Calculation of Stainless Steel Bars

Weight of  Stainless Steel Round Bar

Dia ( mm ) X  Dia (mm ) X 0.00623  = Wt. Per. Mtr.

Dia ( mm ) X  Dia (mm ) X 0.0019    = Wt. Per. Feet.

Weight of Stainless Steel Square Bar

Dia ( mm ) X  Dia ( mm ) X 0.00788 = Wt. Per. Mtr

Dia ( mm ) X  Dia ( mm ) X 0.0024   =  Wt.Per. Feet.

Weight of Stainless Steel Hexagonal Bar

Dia ( mm )     X  Dia ( mm ) X 0.00680    =  Wt. Per.Mtr

Width ( mm ) X  Dia ( mm )  X 0.002072 =  Wt. Per Feet

Weight of Stainless Steel Flat Bar

Width  (mm ) X  Thick ( mm ) X 0.00798 = Wt.Per Mtr.

Width  (mm ) X  Thick ( mm ) X 0.00243 = Wt.Per Feet.

PREN for various Grades of Stainless Steel

What is PREN?

Pitting resistance equivalent numbers (PREN) are a theoretical way of comparing the pitting corrosion resistance of various types of stainless steels, based on their chemical compositions. In general, the higher PREN-value, the more resistant is the stainless steel to localized pitting corrosion by chloride. The elements which have a significant impact are chromium, molybdenum and nitrogen.

The formula used to calculate PREN is as below:

PREN = %Cr + 3.3(%Mo) + 16(%N)

PREN = 1 × %Cr + 3.3 (%Mo + 0.5 × %W) + 16 × %N

Grade Type Cr Mo N PREN
Ferritic
1.4003 10.5-12.5 NS 0.030 max 10.5-12.5
1.4016 430 16.0-18.0 NS NS 16.0-18.0
1.4113 434 16.0-18.0 0.9-1.4 NS 19.0-22.6
1.4509 441 17.5-18.5 NS NS 17.5-18.5
1.4521 444 17.0-20.0 1.8-2.5 0.030max 23.0-28.7
Austenitic
1.4301 304 17.5-19.5 NS 0.11max 17.5-20.8
1.4311 304LN 17.5-19.5 NS 0.12-0.22 19.4-23.0
1.4401/4 316/316L 16.5-18.5 2.0-2.5 0.11max 23.1-28.5
1.4435 316L (2.5% min Mo) 17.0-19.0 2.5-3.0 0.11max 25.3-30.7
1.4406 316LN 16.5-18.5 2.0-2.5 0.12-0.22 25.0-30.3
1.4539 904L 19.0-21.0 4.0-5.0 0.15max 32.2-39.9
1.4563 Sanicro 28 24.0-26.0 3.0-4.0 0.11max 35.9-43.0
1.4547 254SMO 19.5-20.5 6.0-7.0 0.18-0.25 42.2-47.6
1.4529 1925hMo 19.0-21.0 6.0-7.0 0.15-0.25 41.2-48.1
1.4565 4565S 24.0-26.0 4.0-5.0 0.30-0.60 42.0-52.1
Duplex
1.40621 2202 22 0.4 0.2 26.5
1.4162 2101LDX 21.0-22.0 0.1-0.8 0.20-0.25 24.5-28.6
1.4362 SAF 2304 22.0-24.0 0.1-0.6 0.05-0.20 23.1-29.2
1.4462 SAF 2205 21.0-23.0 2.5-3.5 0.10-0.22 30.8-38.1
1.44102 SAF 2507 24.0-26.0 3.0-4.0 0.24-0.35 > 40.2
1.45012 Zeron 1002 24.0-26.0 3.0-4.0 0.20-0.30 > 40.2
1.45072 Ferrinox 2552 24.0-26.0 3.0-4.0 0.20-0.30 > 40.2

Alternative Grades to Stainless Steel 304L Grade

Features
303 Stainless steel 303 grade can be used when higher machinability is needed, and lower corrosion resistance, formability and weldability are acceptable.
316 Stainless steel 316 grade can be used when higher resistance to pitting and crevice corrosion is required, in chloride environments.
321 Stainless steel 321 grade can be used when better resistance to temperatures of around 600-900°C is needed. 321 has higher hot strength.
3CR12 Stainless steel 3CR12 can be used when lower cost is required, and the reduced corrosion resistance and resulting discoloration are acceptable.
430 Stainless steel 430 grade is acceptable when a lower cost is required, and the reduced corrosion resistance and fabrication characteristic are acceptable.

Service Temperature of Various Grades of Stainless Steel

Grade Intermittent service temperature Continuous service temperature
304 1600°F 1700°F
(870°C) (925°C)
316 1600°F 1700°F
(870°C) (925°C)
309 1800°F 2000°F
(980°C) (1095°C)
310 1900°F 2100°F
(1035°C) (1150°C)
410 1500°F 1300°F
(815°C) (705°C)
420 1350°F 1150°F
(735°C) (620°C)
430 1600°F 1500°F
(870°C) (815°C)

Testing of Stainless Steel Bars

  • Manufacturer’s Test Certificate is Provided – Our materials undergo strict quality tests before dispatching them to our clients. All are materials are supplied with Mill Test Certificates, as per EN 10204 3.1
  • Various Testing: Mechanical Testing, Hardness Test, Chemical Analysis, Positive Material Identification (PMI), Flattening Test, Micro and Macro Test, Pitting Resistance Test, Flaring Test, Intergranular Corrosion (IGC) Test.

Testing of Stainless Steel Bright Bars

  • Manufacturer’s Test Certificate is Provided – Our materials undergo strict quality tests before dispatching them to our clients. All are materials are supplied with Mill Test Certificates, as per EN 10204 3.1
  • Various Testing: Mechanical Testing, Hardness Test, Chemical Analysis, Positive Material Identification (PMI), Flattening Test, Micro and Macro Test, Pitting Resistance Test, Flaring Test, Intergranular Corrosion (IGC) Test.

Marking of Stainless Steel Bright Bars

As a standard, Asiamet provides all stainless steel rod marked with Manufacturers Name, Size and Heat No., which can be co related with the test certificate for the product.

Documents Provided to Domestic & Overseas Customers

Certificate of Origin Legalized/Attested by Chamber of Commerce or Embassy
Commercial Invoice including HS Code
Packing List including number of boxes, net weight and gross weight, Marks and Numbers
Fumigation Certificates
Raw Material Test Reports
Heat Treatment Charts
Material Traceability Records
Quality Assurance Plan (QAP)
NABL Approved Laboratory Test Reports

Reviews

There are no reviews yet.

Be the first to review “304L Stainless Steel Bright Bars”

Your email address will not be published. Required fields are marked *