Description
Stainless Steel 904L Coils, N08904, 1.4539 SS coils, 904L Stainless Steel Coils Supplier in India
We Deliver The Highest Quality Stainless Steel N08904, 1.4539, 904L SS Coils! Asiamet is a full line distributor of stainless steel 904L coils. We can offer various value added services such as cut-to-length, polishing, bending, rolling, shearing, manual or automated punching & forming, and welding (MIG, TIG & spot welding). 904 stainless steel coils are available in stock.
Common widths of stainless steel coil is 1000mm, 1250mm and 1500mm. Stainless steel coils can be cut as per clients requirements into sheets. Asiamet carries a wide range of thickness 0.1mm is the thinnest gauge going up until 8.0 mm in stainless steel coils.
It has high molybdenum and extremely low carbon content. Copper content in the alloy greatly improves resistance to strong reducing acids, especially (H2SO4) sulphuric acid. 904L has better resistance. Ti chloride attack against both stress corrosion cracking and crevice / pitting corrosion. With excellent weldability and formability 904L also maintain non-magnetic state in all conditions. 904L provides excellent toughness , even down to cryogenic temperatures with its austenitic structure. It has a higher corrosion resistance than regular steel and is widely used because of the ease in which it is formed into various shapes.
Stainless steel 904 coil is used to manufacture products in a variety of industries where extreme conditions may exist such as marine, oil & gas, chemical processing, power generation, food processing, wastewater and other applications. Asiamet is a stockist, supplier and exporter of high quality stainless steel coil as per ASTM A240 in various sizes and grades such as 304/304L, 310/310S, 316/316L/316Ti, 321/321H, 347/347H & Duplex 2205.
Stainless steel 904/904L coil is typically sold in the annealed condition and is available in 0.1mm to 6.0mm in cold rolled and hot rolled form. Our 304 stainless steel coils come in both 2B finish and various polished finishes such as 2D, BA, No.1, No.4, No.8, 8K, Mirror and Matte, with PVC Coating.
Due to its anti-corrosive properties, stainless steel coils have become essential in the composition of parts for the medical, tooling, mechanical and food industries. Stainless steel coils are widely used in various industries as mentioned in the below table.
Standard Welding Processes for UNS N08904, 1.4539 SS Coils, Stainless Steel 904 Coils
| TIG-Welding |
Arc Welding (E) |
| MAG-Welding Solid Wire |
Laser Beam Welding |
Production & Stock Range for Stainless Steel 904 Coils, UNS N08904, 1.4539 SS Coils
| Product |
Stainless Steel 904 Coils |
| Standard |
ASTM A240, AISI, EN |
| Thickness |
0.1mm-8.0mm |
| Width |
1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm |
| Length |
Custom Cut length, Coil form |
| Surface |
2B, 2D, BA, NO.1, NO.4, NO.8, 8K, Mirror, Checkered, Embossed, Hair Line, Brush Finish, Etching |
| Type |
Hot Rolled Stainless Steel Sheets (HR 2.5mm to 6mm), Cold Rolled Stainless Steel Sheets (CR 0.1mm to 6mm) |
| Shape |
Flat |
| Value Added Services |
Laser Cutting, Polishing, Grinding, Heat Treating, Saw Cutting, Forming, Rolling, Shearing |
| Manufacturers |
Jindal, POSCO, Aperam, TISCO, Outokumpu |
| Origin of Goods |
India, Europe, Japanese, UK, Korea, Thailand, Taiwan. |
| Export Countries |
Saudi Arabia, Tanzania, Africa, Nigeria, Qatar, Oman, UAE and Other Middle East Nations |
| Delivery Time |
Immediate for Goods in Ready Stock, 10-40 Days for Production QTY’s |
| Packing |
Wooden Pallets, Export Sea-Worthy Packing |
| Applications |
Off-Shore Oil Drilling Companies, Power Generation, Petrochemicals, Gas Processing, Specialty Chemicals, Pharmaceuticals, Pharmaceutical Equipment, Chemical Equipment, Sea Water Equipment, Heat Exchangers, Condensers, Pulp and Paper Industry |
| Test Certificates |
As per EN 10204 3.1 |
| Inspection |
Seller Inspection, Buyer Inspection or Third Party Inspection |
Chemical Composition (%) of Stainless Steel 904 Coils, UNS N08904, 1.4539 SS Coils
| Grade |
C |
Mn |
Si |
P |
S |
Cr |
Mo |
Ni |
Cu |
| 904 |
0.02 |
2 |
1 |
0.04 |
0.03 |
19.00 – 23.00 |
4.00 – 5.00 |
23.00 – 28.00 |
1.00 – 2.0 |
Mechanical Properties of Stainless Steel 904 Coils, UNS N08904, 1.4539 SS Coils
| GRADE |
Tensile Strength : Unit – ksi (MPa) , Minimum |
Yeild Strength : 0.2 % Offset , Unit – ksi (MPa) , Minimum |
Elongation : in 2″, Unit : % , Minimum |
| 904 |
71 (490) |
31(215) |
35 |
Equivalents of Various Grades of Stainless Steel 904L Coils, UNS N08904, 1.4539 SS Coils
| STANDARD |
WERKSTOFF NR. |
UNS |
JIS |
BS |
GOST |
AFNOR |
EN |
| SS 904L |
1.4539 |
N08904 |
SUS 904L |
904S13 |
STS 317J5 |
Z2 NCDU 25-20 |
X1NiCrMoCu25-20-5 |
Chemical Composition of Various Grades of Stainless Steel Coils
| Grade |
C≤ |
Si≤ |
Mn≤ |
P≤ |
S≤ |
Ni |
Cr |
| 201 |
0.15 |
1 |
5.5-7.5 |
0.5 |
0.03 |
3.50-5.50 |
16.00-18.00 |
| 202 |
0.15 |
1 |
7.5-10.0 |
0.5 |
0.03 |
4.00-6.00 |
17.00-19.00 |
| 304 |
0.08 |
1 |
2 .00 |
0.045 |
0.03 |
8.00-11.00 |
18.00-20.00 |
| 304L |
0.03 |
1 |
2 .00 |
0.045 |
0.03 |
8.00-12.00 |
18.00-20.00 |
| 309 |
0.2 |
1 |
2 .00 |
0.04 |
0.03 |
12.00-15.00 |
22.00-24.00 |
| 309S |
0.08 |
1 |
2 .00 |
0.045 |
0.03 |
12.00-15.00 |
22.00-24.00 |
| 310 |
0.25 |
1.5 |
2 .00 |
0.04 |
0.03 |
19.00-22.00 |
24.00-26.00 |
| 310S |
0.08 |
1 |
2 .00 |
0.045 |
0.03 |
19.00-22.00 |
24.00-26.00 |
| 316 |
0.08 |
1 |
2 .00 |
0.045 |
0.03 |
10.00-14.00 |
16.00-18.00 |
| 316L |
0.03 |
1 |
2 .00 |
0.045 |
0.03 |
10.00-14.00 |
16.00-18.00 |
| 316Ti |
0.08 |
1 |
2 .00 |
0.045 |
0.03 |
10.00-14.00 |
16.00-18.00 |
| 410 |
0.15 |
1 |
1 .00 |
0.04 |
0.03 |
0.6 |
11.50-13.50 |
| 430 |
0.12 |
0.12 |
1 |
0.04 |
0.03 |
0.6 |
16.00-18.00 |
Mechanical Properties of Stainless Steel Coils
| Grades |
Density |
Melting Point |
Tensile Strength (min.) |
Yield Strength (0.2%Offset) (min.) |
Elongation (min.) |
| 304 |
8.0 g/cm3 |
1400 °C (2550 °F) |
Psi – 75000 , MPa – 515 |
Psi – 30000 , MPa – 205 |
35% |
| 304H |
8.0 g/cm3 |
1400 °C (2550 °F) |
Psi – 75000 , MPa – 515 |
Psi – 30000 , MPa – 205 |
35% |
| 304L |
8.0 g/cm3 |
1400 °C (2550 °F) |
Psi – 75000 , MPa – 515 |
Psi – 30000 , MPa – 205 |
35% |
| 310 |
7.9 g/cm3 |
1402 °C (2555 °F) |
Psi – 75000 , MPa – 515 |
Psi – 30000 , MPa – 205 |
40% |
| 316 |
8.0 g/cm3 |
1400 °C (2550 °F) |
Psi – 75000 , MPa – 515 |
Psi – 30000 , MPa – 205 |
35% |
| 316L |
8.0 g/cm3 |
1399 °C (2550 °F) |
Psi – 75000 , MPa – 515 |
Psi – 30000 , MPa – 205 |
35% |
| 316TI |
8.0 g/cm3 |
1399 °C (2550 °F) |
Psi – 75000 , MPa – 515 |
Psi – 30000 , MPa – 205 |
35% |
| 317 |
7.9 g/cm3 |
1400 °C (2550 °F) |
Psi – 75000 , MPa – 515 |
Psi – 30000 , MPa – 205 |
35% |
| 317L |
7.9 g/cm3 |
1400 °C (2550 °F) |
Psi – 75000 , MPa – 515 |
Psi – 30000 , MPa – 205 |
35% |
| 321 |
8.0 g/cm3 |
1457 °C (2650 °F) |
Psi – 75000 , MPa – 515 |
Psi – 30000 , MPa – 205 |
35% |
| 347 |
8.0 g/cm3 |
1454 °C (2650 °F) |
Psi – 75000 , MPa – 515 |
Psi – 30000 , MPa – 205 |
35% |
| 904L |
7.95 g/cm3 |
1350 °C (2460 °F) |
Psi – 71000 , MPa – 490 |
Psi – 32000 , MPa – 220 |
35% |
| 446 |
7.5 g/cm3 |
1510 °C (2750 °F) |
Psi – 75,000 , MPa – 485 |
Psi – 40,000 , MPa – 275 |
20% |
PREN for various Grades of Stainless Steel Coils
What is PREN?
Pitting resistance equivalent numbers (PREN) are a theoretical way of comparing the pitting corrosion resistance of various types of stainless steels, based on their chemical compositions. In general, the higher PREN-value, the more resistant is the stainless steel to localized pitting corrosion by chloride. The elements which have a significant impact are chromium, molybdenum and nitrogen.
The formula used to calculate PREN is as below:
PREN = %Cr + 3.3(%Mo) + 16(%N)
PREN = 1 × %Cr + 3.3 (%Mo + 0.5 × %W) + 16 × %N
| Grade |
Type |
Cr |
Mo |
N |
PREN |
| Ferritic |
|
|
|
|
|
| 1.4003 |
– |
10.5-12.5 |
NS |
0.030 max |
10.5-12.5 |
| 1.4016 |
430 |
16.0-18.0 |
NS |
NS |
16.0-18.0 |
| 1.4113 |
434 |
16.0-18.0 |
0.9-1.4 |
NS |
19.0-22.6 |
| 1.4509 |
441 |
17.5-18.5 |
NS |
NS |
17.5-18.5 |
| 1.4521 |
444 |
17.0-20.0 |
1.8-2.5 |
0.030max |
23.0-28.7 |
| Austenitic |
|
|
|
|
|
| 1.4301 |
304 |
17.5-19.5 |
NS |
0.11max |
17.5-20.8 |
| 1.4311 |
304LN |
17.5-19.5 |
NS |
0.12-0.22 |
19.4-23.0 |
| 1.4401/4 |
316/316L |
16.5-18.5 |
2.0-2.5 |
0.11max |
23.1-28.5 |
| 1.4435 |
316L (2.5% min Mo) |
17.0-19.0 |
2.5-3.0 |
0.11max |
25.3-30.7 |
| 1.4406 |
316LN |
16.5-18.5 |
2.0-2.5 |
0.12-0.22 |
25.0-30.3 |
| 1.4539 |
904L |
19.0-21.0 |
4.0-5.0 |
0.15max |
32.2-39.9 |
| 1.4563 |
Sanicro 28 |
24.0-26.0 |
3.0-4.0 |
0.11max |
35.9-43.0 |
| 1.4547 |
254SMO |
19.5-20.5 |
6.0-7.0 |
0.18-0.25 |
42.2-47.6 |
| 1.4529 |
1925hMo |
19.0-21.0 |
6.0-7.0 |
0.15-0.25 |
41.2-48.1 |
| 1.4565 |
4565S |
24.0-26.0 |
4.0-5.0 |
0.30-0.60 |
42.0-52.1 |
| Duplex |
|
|
|
|
|
| 1.40621 |
2202 |
22 |
0.4 |
0.2 |
26.5 |
| 1.4162 |
2101LDX |
21.0-22.0 |
0.1-0.8 |
0.20-0.25 |
24.5-28.6 |
| 1.4362 |
SAF 2304 |
22.0-24.0 |
0.1-0.6 |
0.05-0.20 |
23.1-29.2 |
| 1.4462 |
SAF 2205 |
21.0-23.0 |
2.5-3.5 |
0.10-0.22 |
30.8-38.1 |
| 1.44102 |
SAF 2507 |
24.0-26.0 |
3.0-4.0 |
0.24-0.35 |
> 402 |
| 1.45012 |
Zeron 1002 |
24.0-26.0 |
3.0-4.0 |
0.20-0.30 |
> 402 |
| 1.45072 |
Ferrinox 2552 |
24.0-26.0 |
3.0-4.0 |
0.20-0.30 |
> 402 |
Alternative Grades to Stainless Steel 904 Grade
| Features |
|
| 303 |
Stainless steel 303 grade can be used when higher machinability is needed, and lower corrosion resistance, formability and weldability are acceptable. |
| 316 |
Stainless steel 316 grade can be used when higher resistance to pitting and crevice corrosion is required, in chloride environments. |
| 321 |
Stainless steel 321 grade can be used when better resistance to temperatures of around 600-900°C is needed. 321 has higher hot strength. |
| 3CR12 |
Stainless steel 3CR12 can be used when lower cost is required, and the reduced corrosion resistance and resulting discoloration are acceptable. |
| 430 |
Stainless steel 430 grade is acceptable when a lower cost is required, and the reduced corrosion resistance and fabrication characteristic are acceptable. |
Service Temperature of Various Grades of Stainless Steel Coils
| Grade |
Intermittent service temperature |
Continuous service temperature |
| 304 |
1600°F |
1700°F |
|
(870°C) |
(925°C) |
| 316 |
1600°F |
1700°F |
|
(870°C) |
(925°C) |
| 309 |
1800°F |
2000°F |
|
(980°C) |
(1095°C) |
| 310 |
1900°F |
2100°F |
|
(1035°C) |
(1150°C) |
| 410 |
1500°F |
1300°F |
|
(815°C) |
(705°C) |
| 420 |
1350°F |
1150°F |
|
(735°C) |
(620°C) |
| 430 |
1600°F |
1500°F |
|
(870°C) |
(815°C) |
Testing of Stainless Steel Coils
- Manufacturer’s Test Certificate is Provided – Our materials undergo strict quality tests before dispatching them to our clients. All are materials are supplied with Mill Test Certificates, as per EN 10204 3.1
- Various Testing: Mechanical Testing, Hardness Test, Chemical Analysis, Positive Material Identification (PMI), Flattening Test, Micro and Macro Test, Pitting Resistance Test, Flaring Test, Intergranular Corrosion (IGC) Test.
Marking of Stainless Steel Coils
As a standard, Asiamet provides all stainless steel coils marked with Manufacturers Name, Size and Heat No., which can be co related with the test certificate for the product.
Packaging of Stainless Steel Coils
Asiamet is one of the best company in for delivery of goods with shortest lead times. Our products like stainless steel coils are packed to ensure that there is no damage in transit.
Documents Provided to Domestic & Overseas Customers
| Certificate of Origin Legalized/Attested by Chamber of Commerce or Embassy |
| Commercial Invoice including HS Code |
| Packing List including number of boxes, net weight and gross weight, Marks and Numbers |
| Fumigation Certificates |
| Raw Material Test Reports |
| Heat Treatment Charts |
| Material Traceability Records |
| Quality Assurance Plan (QAP) |
| NABL Approved Laboratory Test Reports |
Reviews
There are no reviews yet.