ASTM B111 Copper & Brass Tubes Suppliers in India

ASTM B111 C44300, C68700, C71500 Copper & Brass Tubes Manufacturers, Suppliers

  • Asiamet is a leading manufacturers in India. Asiamet as pride in providing a whole range of high class customization and innovative ASTM B111 A44300, C68700 and C71500 copper & brass tubes using state of art technology. Our range includes.
  • ASTM B111 copper & brass pipe is often used for underground water lines, flexible metal hoses and electrical conduit, along with many others.
  • We have been supplying high quality ASTM B111 A44300, C68700 and C71500 copper & brass tubes with most advance technology and with most reliable quality.
  • Related Keyword- ASTM B111 Copper Tubes, C44300 Copper Tubes, C44300 Admiralty Brass Tubes, C44300 Admiralty Brass Pipes, C68700 Copper Tubes, C68700 Aluminum Brass Tubes, C68700 Aluminum Brass Pipes, C70600 Copper Tubes, C70600 Brass Pipes, C70400 Copper Tubes, C70400 Brass Tubes and Pipes, C70400 Copper-Nickel Tubes and Pipes.
Product ASTM B111 C44300, C68700, C71500 Copper & Brass Tubes
Size (OD) 6mm to 100 mm.
Thickness 0.5 to 25mm.
Length Single random length/ Double random length
Grade C44300, C68700, C70400, C70600, C71500, C71640.
Delivery Immediate, 7-30 Days
Price Terms Ex-Work, FOB, CIF, CFR, CNF
Prices Call +919619672006
Email sales@asiametsteel.com
ASTM B111 Copper & Brass Tubes Manufacturers, Suppliers
  • Do you want to know how much does a ASTM B111 C44300, C68700, C17500 copper & brass tube cost ? Do you want to know where you can get the best price and quality A44300, C68700, C17500 copper & brass tubes?

  • We are ready to provide you our quality products, fast delivery service, and custom pipe sizes. Send us your detailed inquiry to us, our professional staff will get back to you with our best solution and costs.

Chemical Composition of ASTM B111 Copper & Brass Tubes

Designation Chemical Composition %
Cu Sn Al As Ni Fe Mn Pb max. Zn
C44300 70.0-73.0 0.9-1.2 0.02-0.06 0.06 max 0.07  Rem
C68700 76.0-79.0 1.8-2.5 0.02-0.06 0.06 max 0.07 Rem
C71500 Rem 29.0-33.0 0.4-1.0 1.0max 0.05 1.0max

Tensile Requirements of ASTM B111 Copper & Brass Tubes

Copper or Copper Alloy UNS NO. Temper Designation Tensile Strength Yield Strength
Standard Former min ksi min ksi
C44300 O61 annealed 45 15
C68700 O61 annealed 50 18
C71500 O61 annealed 52 18

Testing for ASTM B111 Copper & Brass Tubes

  • Expansion Test-Tube specimens selected for test shall withstand the expansion shown in standard when expanded in accordance with Test Method B 153. The expanded tube shall show no cracking or rupture visible to the unaided eye. Hard-drawn tubes not end annealed are not subject to this test. When tubes are specified end annealed, this test is required and shall be performed on the annealed ends of the sampled tubes.Tubes for ferrule stock are not subject to the expansion test.
  • Flattening Test- Test Method—each test specimen shall be flattened in a press at three (3) places along the length, each new place to be rotated on its axis approximately one third turn from the last flattened area. Each flattened area shall be at least 2 in. in length. A flattened test-specimen shall allow a micrometer caliper set at three (3) times the wall thickness to pass freely over the flattened area. The flattened areas of the test specimen shall be inspected for surface defects.  During inspection, the flattened areas of the test- specimen shall be free of defects, but blemishes of a nature that do not interfere with the intended application are acceptable. Tubes for ferrule stock are not subject to flattening test.
  • Residual Stress Test- A residual stress test is required to be performed only for Copper Alloy UNS Nos. C23000, C28000, C44300, C44400, C44500, C60800, C61300, C61400, and C68700. Unless otherwise specified, the producer shall have the option of testing the product to either the miraculous nitrate test, Test Method B 154, or the ammonia vapor test, Test Method B 858, as prescribed below.
  • Nondestructive Testing- Eddy-Current Test—each tube shall be passed through an eddy-current testing unit adjusted to provide information on the suitability of the tube for the intended application. Testing shall follow the procedures of Practice E 243.
  • Hydrostatic Test- Each tube shall stand, without showing evidence of leakage, an internal hydro static pressure sufficient to subject the material to a fiber stress of 7000 psi [48 MPa] as determined by the following equation for thin hollow cylinders under tension. The tube need not be tested at a hydrostatic pressure of over 1000 psi [7.0 MPa] unless so specified.

Application of ASTM B111 Copper & Brass Tubes

  • It can be also used in structural parts
  • Brass bars are widely used in air conditioners
  • Refrigerators, eclectics due to its highly corrosion-resistant